All the foamed concrete samples were made in house. The sta-ble foam was produced using foam generator Portafoam TM2 Sys-tem, obtained from the Malaysian manufacturer (www.portafoam.com). This system runs from an air compressor and consists of amain generating unit, a foaming unit, and a lance unit. The foamingagent used was Noraite PA-1 (protein based) which is appropriatefor foamed concrete densities ranging from 600 kg/m3to 1600 kg/m3. Noraite PA-1 comes from natural sources and has a weight ofaround 80 g/l and expands about 12.5 times when used with thePortafoam foam generator. Three identical specimens were pre-pared for each density and were tested at 28 days after mixing
عنوان انگلیسی مقاله: Mechanical properties of foamed concrete exposed to high temperatures
عنوان فارسی مقاله: خواص مکانیکی بتن فومی در معرض دمای بالا
دسته: عمران - مهندسی مواد
فرمت فایل ترجمه شده: WORD (قابل ویرایش)
تعداد صفحات فایل ترجمه شده: 46
ترجمه ی سلیس و روان مقاله آماده ی خرید می باشد.
_______________________________________
چکیده ترجمه:
این
مقاله نتایج حاصل از یک مطالعه تجربی و تحلیلی را در بررسی خواص مکانیکی
فوم بتنی در معرض دمای بالا گزارش میدهد. دو چگالی بتن فومی، 650 و 1000
kg/m3، ساخته شدند و با بررسی های اضافی بر چگالیهای 800، 1200 و 1400
kg/m3 برای داده های اضافی مورد بررسی قرار گرفت. نتایج تجربی دائما ثابت
میکند که کاهش سختی بتن فومی در دماهای بالا عمدتا پس از 90 درجه
سانتیگراد بدون در نظر گرفتن چگالی رخ می دهد وقتی که آب منبسط می شود و از
جسم متخلخل تبخیر میشود.از مقایسه نتایج تجربی این پژوهش با تعدادی از مدل
های پیش بینی برای مقاومت معمولی بتن ، این تحقیقات نشان داده که خواص
مکانیکی بتن فومی میتواند با استفاده از خواص مکانیکی مدل ها برای وزن
نرمال بتن داده شده پیش بینی شود که خواص مکانیکی بتن فومی از سیمان پرتلند
CEM1 نتیجه میشود.
کلیدواژه: بین فومی، خواص مکانیکی، دمای بالا، دمای مرتفع، مدل بتن، مدل پیش بینی قدرت، تنش- کرنش، بتن در آنش